PENGARUH FRAKSI VOLUME SERBUK ARANG TEMPURUNG KELAPA DENGAN SERBUK CANGKANG KERANG DARAH TERHADAP KEKERASAN DAN KEAUSAN PADA POLYMER MATRIX COMPOSITE
EFFECT OF VOLUME FRACTION OF COCONUT SHELL CHARCOAL POWDER WITH BLOOD SHELL SHELL POWDER ON HARDNESS AND WEAR OF POLYMER MATRIX COMPOSITE

disusun oleh AHMAD AMIN SYAFII


SubyekMaterial kampas rem
Arang Tempurung kelapa
Cangkang kerang darah
Pengujian kekerasan (Shore D ASTM D2240)
Pengujian keausan (Metode Ogoshi ASTM G99-95a)
Kata KunciMaterial kampas rem
Arang Tempurung kelapa
Cangkang kerang darah
Pengujian kekerasan (Shore D ASTM D2240)
Pengujian keausan (Metode Ogoshi ASTM G99-95a)

[ Anotasi Abstrak ]

Kemajuan teknologi otomotif memicu permintaan perangkat kendaraan yang aman. Rem adalah komponen yang sangat penting dalam kendaraan karena berfungsi untuk mengurangi energi kinetik kendaraan guna menjaga keselamatan pengendara. Indonesia kaya akan sumber daya alam yang melimpah dan harus dijaga kelestariannya dengan memanfaatkan limbah tempurung kelapa dan limbah cangkang kerang darah yang belum dimanfaatkan secara optimal dan efektif. Penelitian ini bertujuan untuk menganalisis pengaruh variasi fraksi volume serbuk arang tempurung kelapa dan cangkang kerang darah terhadap sifat mekanis komposit matriks polimer, khususnya kekerasan dan keausan. Uji kekerasan dilakukan menggunakan metode Shore D sesuai standar ASTM D2240, sementara uji keausan dilakukan menggunakan metode Ogoshi sesuai standar ASTM G99-95a. Variasi fraksi volume meliputi 10%, 20%, 30%, 40%, dan 50%, dengan tiga kali pengulangan untuk setiap spesimen. Hasil pengujian menunjukkan bahwa peningkatan fraksi serbuk cangkang kerang darah memberikan kontribusi signifikan terhadap peningkatan kekerasan. Nilai kekerasan optimal ditemukan pada fraksi volume 10%-50% dengan rata-rata 85,50 SHD, memenuhi standar SNI untuk kekerasan kampas rem. Sebaliknya, nilai keausan spesifik cenderung menurun dengan bertambahnya fraksi serbuk cangkang kerang darah. Fraksi dengan nilai keausan paling optimal pada fraksi volume 10%-50% yang mencapai rata-rata 6,1038×10-4 mm²/kg, berada dalam rentang nilai standar SNI 5×10⁻⁴ mm²/kg 5×10⁻³ mm²/kg. Hasil penelitian mengindikasikan bahwa komposisi cangkang kerang darah memiliki sifat tribologi yang lebih baik dibandingkan serbuk tempurung kelapa. Penggunaan cangkang kerang darah sebagai bahan alternatif dapat meningkatkan performa mekanik dan menurunkan laju keausan pada material komposit berbasis polimer.


Deskripsi Lain

The advancement of automotive technology has triggered a demand for safe vehicle components. Brakes are a crucial component in vehicles they function to reduce the vehicle's kinetic energy to ensure rider safety. Indonesia is rich in abundant natural resources, which must be preserved by utilizing coconut shell waste and blood clam shell waste that have not been optimally and effectively utilized. This study aims to analyze the effect of varying volume fractions of coconut shell charcoal powder and blood clam shells on the mechanical properties of polymer matrix composites, particularly hardness and wear resistance. Hardness testing was conducted using the Shore D method following ASTM D2240 standards, while the wear rate test was performed using the Ogoshi method according to ASTM G99-95a standards. The volume fraction variations included 10%, 20%, 30%, 40%, and 50%, with three repetitions for each specimen. The test results showed that an increase in the fraction of blood clam shell powder contributed significantly to the increase in hardness. The optimal hardness value was found at a volume fraction of 10%50%, with an average of 85.50 SHD, meeting the Indonesian National Standard (SNI) for brake pad hardness. Conversely, the specific wear rate value tended to decrease the fraction of blood clam shell powder increased. The optimal wear rate value was found in the 10%-50% volume fraction, reaching an average of 6.1038×10⁻⁴ mm²/kg, within the SNI standard range of 5×10⁻⁴ mm²/kg 5×10⁻³ mm²/kg. The research results indicate that the composition of blood clam shells has better tribological properties compared to coconut shell powder. The use of blood clam shells an alternative material can enhance mechanical performance and reduce wear rates in polymer-based composite materials.

Kontributor: Dr. Mahrus Khoirul Umami, S.T., M.Sc; Mirza Pramudia, S.T., M.Eng., M.Pr
Tanggal tercipta: 2025-01-09
Jenis(Tipe): Text
Bentuk(Format): pdf
Bahasa: Indonesia
Pengenal(Identifier): TRUNOJOYO-Tugas Akhir-35111
No Koleksi: 200481100024


Ketentuan (Rights) :
2025

 Download File Penyerta (khusus anggota terdaftar)

 File PDF  1. TRUNOJOYO-Tugas Akhir-35111-Abstract.pdf - 272 KB
 File PDF  2. TRUNOJOYO-Tugas Akhir-35111-Cover.pdf - 724 KB
 File PDF  3. TRUNOJOYO-Tugas Akhir-35111-Chapter1.pdf - 494 KB
 File PDF  4. TRUNOJOYO-Tugas Akhir-35111-Chapter2.pdf - 1383 KB
 File PDF  5. TRUNOJOYO-Tugas Akhir-35111-Chapter3.pdf - 1849 KB
 File PDF  6. TRUNOJOYO-Tugas Akhir-35111-Chapter4.pdf - 1080 KB
 File PDF  7. TRUNOJOYO-Tugas Akhir-35111-Conclusion.pdf - 484 KB
 File PDF  8. TRUNOJOYO-Tugas Akhir-35111-References.pdf - 465 KB
 File PDF  9. TRUNOJOYO-Tugas Akhir-35111-Appendices.pdf - 5085 KB


 Dokumen sejenis...

     Tidak ada !

 Dokumen yang bertautan...





 Kembali ke Daftar