PENGARUH VARIASI KECEPATAN EKSTRUDER, VARIASI INITIAL TEMPERATUR, DAN VARIASI JENIS PLASTIK TERHADAP KEKUATAN TARIK KOMPOSIT RESIN
THE EFFECT OF VARIATION OF EXTRUDER SPEED, INITIAL TEMPERATURE VARIATION, AND VARIATION OF PLASTIC TYPES ON COMPOSITE RESIN TENSION STRENGTH
disusun oleh MOHYAMMAD HISYAM
| Subyek: | Spesimen Komposit Resin RAL Jenis Plastik Suhu Ekstruder Putaran Ulir Ekstruder Kekuatan Tarik |
| Kata Kunci: | Spesimen Komposit Resin RAL Jenis Plastik Suhu Ekstruder Putaran Ulir Ekstruder Kekuatan Tarik |
[ Anotasi Abstrak ]
Penggunaan plastik dan barang- barang berbahan plastik dalam kehidupan manusia semakin hari semakin meningkat. Peningkatan penggunaan plastik di Indonesia mencapai rata-rata 200 ton pertahun. Plastik. Daur ulang (Reycle) merupakan salah satu proses yang mudah dan banyak dilakukan untuk merubah sampah plastik yang tidak termanfaatkan menjadi sesuatu yang berguna dan bernilai adalah dengan membuat bahan baku tekstil. Salah satau cara daur ulang yang dilakukan membuat serat plastik yang berguna untuk penguat material komposit resin. Metode yang digunakan untuk mencari komposisi terbaik adalah dengan menggunkan ( Design Of Experiment) RAL 23 dimana faktornya adalah jenis plastik, Suhu mesin Ekstruder, dan Putaran ulir ekstruder. Sedangkan responnya yaitu kekuatan tarik spesimen komposit resn dengan satuan Newton/mm2. Sedangkan Kombinasi terbaik dengan rata- rata kekuatan tarik 25,1633 N/mm2 adalah ( kombinasi A1 B2 C2), yaitu Jenis plastik dengan kode level 1 (HDPE), Faktor B (suhu extruder) dengan kode level 2 (3000) dan faktor C (putaran ulir) dengan kode level 2 (45 rpm).
Deskripsi Lain
The use of plastic and plastic goods in human life is increasingly increasing. The increase in plastic use in Indonesia reaches an average of 200 tons per year. Reycle is one of the easy processes and is mostly done to change plastic waste that is not utilized into something useful and valuable by making textile raw materials. One of the methods of recycling is making plastic fibers useful for reinforcing resin composite materials. The method used to find the best composition is to use (Design Of Experiment) RAL 23 where the factors are type of plastic, machine temperature of extruder, and round screw extruder. While the response is the tensile strength of composite samples in Newton / mm2 units. While the best combination with an average tensile strength of 25.1633 N / mm2 is (a combination of A1 B2 C2), which is a type of plastic with code level 1 (HDPE), Factor B (extruder temperature) with code level 2 (3000) and factor C (thread rotation) with code level 2 (45 rpm).
| Kontributor | : Dr.RAHMAD HIDAYAT, S.T.,M.T ; MU\\\'ALIM, S.T., M.T |
| Tanggal tercipta | : 2019-01-10 |
| Jenis(Tipe) | : Text |
| Bentuk(Format) | |
| Bahasa | : Indonesia |
| Pengenal(Identifier) | : TRUNOJOYO-Tugas Akhir-15013 |
| No Koleksi | : 140421100108 |
Download File Penyerta (khusus anggota terdaftar)
1. TRUNOJOYO-Tugas Akhir-15013-Cover.pdf - 885 KB 2. TRUNOJOYO-Tugas Akhir-15013-Abstract.pdf - 268 KB 3. TRUNOJOYO-Tugas Akhir-15013-Chapter 1.pdf - 261 KB 4. TRUNOJOYO-Tugas Akhir-15013-Chapter 2.pdf - 662 KB 5. TRUNOJOYO-Tugas Akhir-15013-chapter 3.pdf - 1440 KB 6. TRUNOJOYO-Tugas Akhir-15013-chapter 4.pdf - 1583 KB 7. TRUNOJOYO-Tugas Akhir-15013-conclusion.pdf - 10 KB 8. TRUNOJOYO-Tugas Akhir-15013-references.pdf - 80 KB 9. TRUNOJOYO-Tugas Akhir-15013-Appendices.pdf - 2313 KB
Dokumen sejenis...Tidak ada !
Dokumen yang bertautan...
Kembali ke Daftar