Pencemaran mikroplastik dari residu mulsa plastik berbahan Linear Low Density Polyethylene (LLDPE) berpotensi merusak sifat kimia tanah dan menghambat pertumbuhan tanaman. Penelitian ini bertujuan menganalisis pengaruh peningkatan dosis paparan mikroplastik LLDPE terhadap sifat kimia tanah serta pertumbuhan bayam hijau (Amaranthus hybridus L.). Metode menggunakan Rancangan Acak Lengkap (RAL) faktor tunggal dengan 5 perlakuan dosis LLDPE berukuran 0,5 mm dan 4 ulangan, yaitu P0 (Kontrol), P1 (25 g), P2 (50 g), P3 (75 g), dan P4 (100 g) dalam 5 kg tanah mediteran. Parameter meliputi pH tanah, N-total tanah, tinggi tanaman, jumlah daun, diameter batang, luas daun, panjang akar, volume akar, diameter akar, bobot basah, dan bobot kering. Hasil menunjukkan paparan mikroplastik LLDPE berpengaruh nyata terhadap seluruh parameter. Hambatan pertumbuhan paling ekstrem terjadi pada P3 (75 gram) dengan menghasilkan luas daun (79,09 cm2rn), volume akar (1,29 ml), diameter akar (0,37 mm), bobot basah (7,15 gram), dan bobot kering (0,65 gram) terendah, disertai pH tanah alkalin (7,61) dan meningkatkan struktur pori serta ketersediaan N berkurang meskipun N-total tinggi (0,08%) namun tidak tersedia bagi tanaman. Pada P4 (100 g), aglomerasi partikel LLDPE mereduksi efek toksik dan meningkatkan water holding capacity, sehingga pertumbuhan relatif lebih baik dibanding P3. Disimpulkan bahwa peningkatan dosis mikroplastik LLDPE secara nyata menurunkan ketersediaan hara tanah dan menekan seluruh parameter pertumbuhan bayam hijau, dengan perlakuan P3 dan P4 menunjukkan penghambatan tertinggi yang tidak berbeda nyata satu sama lain. Disarankan penelitian lanjutan mengkaji serapan hara P dan K serta akumulasi residu LLDPE pada jaringan tanaman.


Deskripsi Lain

Microplastic contamination from agricultural mulch film residues made of Linear Low-Density Polyethylene (LLDPE) potentially disrupts soil chemical properties and inhibits plant growth. This study analyzed the effect of increasing LLDPE microplastic doses on soil chemical properties and growth of green spinach (Amaranthus hybridus L.) using a single-factor Completely Randomized Design (CRD) with 5 dose treatments (0.5 mm particle size) and 4 replications: P0 (Control), P1 (25 g), P2 (50 g), P3 (75 g), and P4 (100 g) mixed into 5 kg of Mediterranean soil. Parameters measured included soil pH, total nitrogen, plant height, leaf number, stem diameter, leaf area, root length, root volume, root diameter, fresh weight, and dry weight. Results showed that LLDPE exposure significantly affected all parameters. The most severe inhibition occurred in P3 (75 g), recording the lowest leaf area (79.09 cm²), root volume (1.29 ml), root diameter (0.37 mm), fresh weight (7.15 g), and dry weight (0.65 g), with alkaline soil pH (7.61) and increasing pore structure and reducing N availability even though total N is high (0.08%) yet unavailable for plant uptake. In P4 (100 g), particle agglomeration reduced toxic effects and improved water-holding capacity, yielding relatively better growth than P3. Increasing LLDPE doses significantly reduced soil nutrient availability and suppressed all growth parameters, with P3 and P4 showing the greatest inhibition and no significant difference between them. Further research on phosphorus and potassium uptake and LLDPE accumulation in leaf tissue is recommended.

• RESPON PEMBERIAN PUPUK ORGANIK DAN MULSA TERHADAP PERTUMBUHAN DAN HASIL TANAMAN BUNCIS (Phaseolus vulgaris L.)
• PEMANFAATAN PERIODE BERO SETELAH PERGILIRAN TANAMAN KEDUA PADA LAHAN KERING DENGAN PEMULSAAN JERAMI TERHADAP PERTUMBUHAN DAN HASIL TANAMAN KACANG HIJAU (Vigna radiata L.)
• PENGARUH PENGGUNAAN MACAM MULSA ORGANIK TERHADAP PERTUMBUHAN DAN HASIL PRODUKSI DUA VARIETAS CABAI RAWIT (Capsicum frutescens L.)
• PENGARUH PEMBERIAN MULSA ORGANIK DAN PUPUK ORGANIK CAIR (POC) URIN SAPI TERHADAP PERTUMBUHAN DAN HASIL BAWANG MERAH (Allium ascalonicum L.)
• RESPON PERTUMBUHAN BAWANG MERAH (Allium ascalonicum L.) TERHADAP APLIKASI MULSA PLASTIK HITAM PERAK DAN PUPUK KANDANG